Testes físico-mecânicos e físico-químicos do couro da tilápia vermelha
Other Titles: 
Physical-mechanical and physical-chemical tests of red tilapia leather
Author(s): 
Institution: 
  • Universidade Estadual de Maringá (UEM)
  • Universidade Estadual Paulista (UNESP)
  • UNIDERP
ISSN: 
0102-0935
Abstract: 
  • Realizaram-se testes físico-mecânicos e físico-químicos em couro de tilápia vermelha (Oreochromis spp.) a fim de testar a sua resistência. As amostras foram distribuídas em delineamento inteiramente ao acaso com dois tratamentos: no T1, procedeu-se à retirada do corpo-de-prova no sentido longitudinal e, no T2, à retirada do corpo-de-prova no sentido transversal. Para os testes de determinação da resistência à tração, alongamento e rasgamento progressivo, foi utilizado o dinamômetro EMIC, com velocidade de afastamento entre as cargas de 100 ± 20mm/min, em ambiente climatizado (± 23ºC e UR do ar de 50%), por 24 horas. A espessura do couro variou de 0,61 a 0,75mm, mas não houve diferença entre os sentidos analisados. O couro apresentou maior resistência à tração no sentido transversal, 25,89N/mm², (P<0,01), comparado ao sentido longitudinal, 14,20 N/mm². O alongamento foi significativamente (P<0,05) maior no sentido longitudinal, 80,8%, em relação ao transversal, 62,6%. Não houve diferença para o rasgamento progressivo entre os tratamentos. O couro apresentou teor de óxido de cromo de 3,8%, graxa de 15,1% e pH e cifra diferencial de 3,5 e 0,5, respectivamente. Os valores nos testes de resistência e físico-químicos apresentados pelo couro indicam que ele pode ser utilizado para a confecção de vestuário e artefatos de couro em geral.
  • Physical-mechanical and physical-chemical tests were carried out on red tilapia leather. They were distributed in a completely randomized design with two treatments: T1 = longitudinal body of proof; T2 = transversal body of proof. It was used the EMIC dynamometer for the tests of resistance to traction and elongation and the progressive tearing, with the speed of 100±20mm/min away between the charges, in an acclimatized room (±23°C and relative humidity of 50%) during 24 hours. The thickness of the analyzed leathers ranged from 0.61 to 0.75mm, without differing between the analyzed ways. The leather demonstrated a higher resistance to traction in the transversal direction (25.89N/mm²) (P<0.01), when compared to the longitudinal one (14.20N/mm²). However, the elongation was significantly higher (P<0.05) in the longitudinal direction (80.8%) when compared to the transversal (62.6%). There was no significant difference for the progressive tearing between the treatments (longitudinal = 18.56N/mm; transversal = 21.90N/mm). The leather demonstrated a content of 3.8% of chromium oxide, 15.1% of grease, and pH and difference value of 3.5 and 0.5, respectively. The values in the resistance and physical-chemical tests shown by the leather indicate that it may be used for clothing and leather artifacts in general.
Issue Date: 
1-Apr-2010
Citation: 
Arquivo Brasileiro de Medicina Veterinária e Zootecnia. Universidade Federal de Minas Gerais, Escola de Veterinária, v. 62, n. 2, p. 475-480, 2010.
Time Duration: 
475-480
Publisher: 
Universidade Federal de Minas Gerais (UFMG), Escola de Veterinária
Keywords: 
  • tilápia
  • couro
  • resistência
  • qualidade
  • fibras colágenas
  • tilapia
  • leather
  • resistance
  • quality
  • collagen fibers
Source: 
http://dx.doi.org/10.1590/S0102-09352010000200030
URI: 
http://hdl.handle.net/11449/578
Access Rights: 
Acesso aberto
Type: 
outro
Source:
http://repositorio.unesp.br/handle/11449/578
Appears in Collections:Artigos, TCCs, Teses e Dissertações da Unesp

There are no files associated with this item.
 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.