Estudo da adsorção e oxidação do monóxido de carbono sobre as fases intermetálicas ordenadas AuIn, AuSb2, AuSn, PdSb e PdSn

Abstract

Aiming to reduce the cost of electrocatalysts and a greater resistance to CO poisoning this work was to study the adsorption and oxidation of carbon monoxide on ordered intermetallic phases AuIn, AuSb2, AuSn, PdSb and PdSn using voltammetric techniques in alkaline electrolyte solution. The results suggest that the AuSn and PdSn intermetallics has some form of resistance to CO poisoning. It is assumed that this behavior is a result of electronic effect and the effect of the third body has been achieved by adding a second metal to Au and Pd. However, further studies should be conducted to confirm this hypothesis as to test these materials as electrocatalysts in the reaction of oxidation of fuels

Visando uma redução no custo dos eletrocatalisadores assim como uma maior resistência ao envenenamento por CO este trabalho teve por objetivo estudar a adsorção e oxidação do monóxido de carbono sobre as fases intermetálicas ordenadas AuIn, AuSb2, AuSn, PdSb e PdSn utilizando técnicas voltamétricas em solução eletrolítica alcalina. Os resultados sugerem que os intermetálicos AuSn e PdSn apresentem algum tipo de resistência ao envenenamento por CO. Supõe-se que este comportamento seja resultante do efeito eletrônico e do efeito do terceiro corpo que foi conseguido com a adição um segundo metal ao Au e ao Pd. No entanto, estudos mais aprofundados devem ser realizados seja para comprovar esta hipótese como para testar estes materiais como eletrocatalisadores na reação de oxidação de combustíveis