Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor
Autor(es): 
Instituição: 
  • Universidade Estadual Paulista (UNESP)
  • Comiss Nacl Energie Nucl
  • Universidade Federal de São Carlos (UFSCar)
ISSN: 
0955-2219
Resumo: 
Zirconia-ceria powders with ceria concentration varying from 0 to 12 mol% were synthesized using a polymeric precursor route based on the Pechini process. Powder characteristics were evaluated with regard to the crystallite size, BET surface area, phase distribution, nitrogen adsorption/desorption behavior, and agglomeration state. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. It was demonstrated that the synthesis method is effective to prepare nanosized powders of tetragonal zirconia single-phase. Sinterability mainly depended on the agglomeration state of powders and the monoclinic phase content, fully tetragonal zirconia ceramic, with grain size of 2.4 mu m, was obtained after addition of at least 9 mol% ceria and sintering at 1500 degrees C for 4 h. (C) 2000 Elsevier B.V. Ltd. All rights reserved.
Data de publicação: 
1-Jul-2000
Citação: 
Journal of the European Ceramic Society. Oxford: Elsevier B.V., v. 20, n. 8, p. 1077-1084, 2000.
Duração: 
1077-1084
Publicador: 
Elsevier B.V.
Palavras-chaves: 
  • CeO2
  • microstructure-final
  • powders-chemical preparation
  • precursors-organic
  • sintering
  • ZrO2
Fonte: 
http://dx.doi.org/10.1016/S0955-2219(99)00269-1
Endereço permanente: 
Direitos de acesso: 
Acesso restrito
Tipo: 
outro
Fonte completa:
http://repositorio.unesp.br/handle/11449/34651
Aparece nas coleções:Artigos, TCCs, Teses e Dissertações da Unesp

Não há nenhum arquivo associado com este item.
 

Itens do Acervo digital da UNESP são protegidos por direitos autorais reservados a menos que seja expresso o contrário.