X-ray powder data and bond valence of La0.65Sr0.35MnO3 after Rietveld refinement
Autor(es): 
Instituição: 
Universidade Estadual Paulista (UNESP)
ISSN: 
0885-7156
Resumo: 
Powder X-ray diffraction (XRD) data were collected for La0.65Sr0.35MnO3 prepared through an alternative method from a stoichiometric mixture of Mn2O3, La2O3, and SrO2, fired at 1300 degreesC for 16 h. XRD analysis using the Rietveld method was carried out and it was found that manganite has rhombohedral symmetry (space group R(3) over bar c). The lattice parameters are found to be a=5.5032 Angstrom and c=13.3674 Angstrom. The bond valence computation indicates that the initial inclusion of Sr occurs at higher temperature. (C) 2002 International Centre for Diffraction Data.
Data de publicação: 
1-Jun-2002
Citação: 
Powder Diffraction. Newtown Sq: J C P D S-int Centre Diffraction Data, v. 17, n. 2, p. 149-152, 2002.
Duração: 
149-152
Publicador: 
J C P D S-int Centre Diffraction Data
Palavras-chaves: 
  • manganite
  • X-ray diffraction
  • Rietveld method
  • perovskite
  • bond valence
Fonte: 
http://dx.doi.org/10.1154/1.1481522
Endereço permanente: 
Direitos de acesso: 
Acesso restrito
Tipo: 
outro
Fonte completa:
http://repositorio.unesp.br/handle/11449/35937
Aparece nas coleções:Artigos, TCCs, Teses e Dissertações da Unesp

Não há nenhum arquivo associado com este item.
 

Itens do Acervo digital da UNESP são protegidos por direitos autorais reservados a menos que seja expresso o contrário.