Defect-induced photoluminescence of powdered silica glass
Autor(es): 
Instituição: 
  • Universidade Federal de São Carlos (UFSCar)
  • Universidade Estadual Paulista (UNESP)
ISSN: 
1012-0386
Resumo: 
Visible photoluminescence was generated in standard soda-lime-silica glass powder, mechanically milled in a high-energy attrition mill. The broad emission band maximum shows a linear dependence on the exciting wavelength, suggesting the possibility to tune the PL emission. The photoluminescence was attributed to defect generation related to unsatisfied chemical bonds due to the high surface area. Raman scattering and ultraviolet-visible optical reflectance measurements corroborate this assertion. Transmission electron microscopy measurements indicate that the powder is composed by nanocrystallites with about 10-20 nanometers immersed in an amorphous media.
Data de publicação: 
27-Mar-2008
Citação: 
Defect and Diffusion Forum, v. 273-276, p. 479-484.
Duração: 
479-484
Palavras-chaves: 
  • Attrition mill
  • Photoluminescence
  • Silica glass
  • Surface defects
  • Emission band
  • High-energy attrition mill
  • Optical reflectance measurements
  • Crystal defects
  • Mechanical alloying
  • Powder metallurgy
  • Reflectometers
  • Transmission electron microscopy
  • Fused silica
Fonte: 
http://dx.doi.org/10.4028/www.scientific.net/DDF.273-276.479
Endereço permanente: 
Direitos de acesso: 
Acesso restrito
Tipo: 
outro
Fonte completa:
http://repositorio.unesp.br/handle/11449/70350
Aparece nas coleções:Artigos, TCCs, Teses e Dissertações da Unesp

Não há nenhum arquivo associado com este item.
 

Itens do Acervo digital da UNESP são protegidos por direitos autorais reservados a menos que seja expresso o contrário.