Structural Evaluation of Mechanically Alloyed and Heat-Treated Ti-25at-%Si Powders
Autor(es): 
Instituição: 
Universidade Estadual Paulista (UNESP)
ISSN: 
0255-5476
Resumo: 
This work discusses on the structural evaluation of mechanically alloyed and heat-treated Ti-25at%Si powders. The milling process was conducted in a planetary ball mill using stainless steel balls/vials, 200 rpm and ball-to-powder weight ratio of 5:1, whereas the heat treatment was conducted under Ar atmosphere at 1100 C for 4 h. Samples were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy and energy dispersive spectrometry. The Si peaks disappeared after milling for 30h, indicating that the Si atoms were dissolved into the Ti lattice in order to form an extended solid solution. The Ti peaks were broadened and their intensities reduced for longer milling times whereas a halo was formed in Ti-25Si powders milled for 200h suggesting that an amorphous structure was achieved. The crystallite size was decreased with increasing milling times. A large Ti3Si amount was found in mechanically alloyed Ti-25at%Si powders after heating at 1100 degrees C for 4h.
Data de publicação: 
1-Jan-2012
Citação: 
Advanced Powder Technology Viii, Pts 1 and 2. Stafa-zurich: Trans Tech Publications Ltd, v. 727-728, p. 227-232, 2012.
Duração: 
227-232
Publicador: 
Trans Tech Publications Ltd
Palavras-chaves: 
  • mechanical alloying
  • titanium alloy
  • hot pressing
Fonte: 
http://dx.doi.org/10.4028/www.scientific.net/MSF.727-728.227
Endereço permanente: 
http://hdl.handle.net/11449/9384
Direitos de acesso: 
Acesso restrito
Tipo: 
outro
Fonte completa:
http://repositorio.unesp.br/handle/11449/9384
Aparece nas coleções:Artigos, TCCs, Teses e Dissertações da Unesp

Não há nenhum arquivo associado com este item.
 

Itens do Acervo digital da UNESP são protegidos por direitos autorais reservados a menos que seja expresso o contrário.