Avaliação do comportamento mecânico sob deformação da liga Ti- 30Ta visando aplicações biomédicas

Abstract

Titanium and its alloys have been used for biomedical applications due their excellent properties such as high corrosion resistance, biocompatibility and mechanical properites. In this study, microstructural and mechanical properties of Ti-30Ta alloy was evaluated during its processing. Ti-30Ta alloy ingots were produced from sheets of commercially pure titanium (99.9%) and tantalum (99.9%). Its melting was realized in arc melting furnace in an argon atmosphere. After homogenizing at 1200ºC, ingots were cold worked by swaging. Samples with 13 mm in diameter were obtained. They were forging at the reduction ratios of 15%. After deformation, microstructure was evaluated by optical microscopy in each condition. Also, Vickers microhardness of samples was measured and phase constitution was evaluated using XRD analysis

Ligas de titânio estão sendo utilizadas em aplicações Biomédicas devido as suas excelentes propriedades, tasi como elevada resistência à corrosão, biocompatibilidade e propriedades mecânicas. Neste trabalho, as propriedades mecânicas e microestrutural da liga de Tu-30Ta são avaliadas durante o processame o de lingotes de Ti-30Ta, que foram produzidos a partir de titânio comercialmente puro (99,9%) e tântalo(99,9%). A fusão foi realizada em um forno a arco elétrico com atmosfera de argônio. O lingote é homogeneizado a 1200 oC, forjado a frio, onde uma amostra de 13mm de diâmetro é obtida. A amostra é forjada até que obtenha uma redução de 15%. Depois da deformação, a microsestrutura é avaliada por microscopia óptica em cada condição. Assim como a microdureza Vicker das amostras, que foram medidas e constituicao de fase foi avaliada pela analise DRX