Influence of the preparation route on the structural, morphological and spectroscopic properties of SrTiO3 and SrTiO3:eu3+ powders

Abstract

This research shows the influence of the synthesis route in the structural and morphological characteristics as well as in the luminescent properties of doped with europium and pure SrTiO3 (STO) powders prepared by microwave assisted hydrothermal synthesis, MWH, and by the polymeric precursor method, PPM. The XRD at room temperature of the STO powders nominally pure obtained by PPM at 700°C for 3 hours, as well as by the MWH at 190°C by 30 minutes present all the reflection peaks for the cubic perovskite structure (JCPDS-ICDD 35-734). The morphology varies according to the synthesis route. The particles of pure STO obtained by PPM presents morphology in the form of plates and the morphology of the particles synthesized by MWH is spherical with approximately 150 nm. The photoluminescent analysis shows for pure STO wide bands associated with the transition of charge transfer from the titanates group (TiO3)2- that are centered on 450 nm. In both preparation methods the emission bands obtained in the composites spectra were found to be asymmetric and low intense. However, in the case of the STO prepared by the PPM a bigger FWHM of the band can be observed. The excitation of the samples was done using a laser (Coherent Innova) with wavelength of 350 nm.