Resistência à flexão em porcelana feldspática: efeito da ciclagem mecânica e limite de fadiga pelo método escada

Abstract

This study evaluated the fatigue limit (FL) by the staircase method and the effect of mechanical cycling on the flexural strength (FS) of Duceragold feldspathic porcelain. Specimens (25 x 5 x 2 mm) were made according to manufacturer’s directions and submitted to three-point flexural strength test (n = 10). To determine FL (n = 30; 10,000 cycles; 2 Hz), an initial loading of 60% of the FS and an incremental loading (step) of 3% of the FS were used. Data were analyzed by Anova and Tukey´s test (p < 0.05). Although the proposed cycles have not reduced FS significantly, fractography analysis showed striation, characteristic signs of mechanical fatigue.

Este estudo avaliou o limite de fadiga (LF), determinado pelo método escada, e o efeito da ciclagem mecânica sobre a resistência à flexão (RF) da porcelana feldspática Duceragold. Corpos de prova (25 x 5 x 2 mm) foram confeccionados de acordo com as instruções do fabricante e submetidos ao ensaio de RF (n = 10), em três pontos. Para determinação do LF (n = 30), foram utilizados carregamento inicial de 60% da RF, tensão incremental de 3% da RF, 10.000 ciclos e 2 Hz. Os dados foram submetidos à Anova e teste de Tukey (p < 0,05). Embora os ciclos propostos não tenham reduzido estatisticamente a RF, análises fractográficas evidenciaram estrias, sinais característicos de fadiga mecânica