Title: 
Efeito da infiltração de sílica pelo método sol-gel na resistência à flexão de bicamadas de porcelana e Y-TZP
Other Titles: 
Effect of silica infiltration by sol-gel method on the flexural strength of porcelain and Y-TZP bilayers
Author(s): 
Reis, Ana Flávia Nunes
Institution: 
Universidade Estadual Paulista (UNESP)
Sponsorship: 
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Abstract: 
  • O objetivo deste trabalho foi infiltrar sílica em uma cerâmica Y-TZP, avaliar seu efeito na resistência à flexão Biaxial, e na união com a porcelana feldspática. Para a análise da resistência à flexão foram confeccionados 180 discos de zircônia, 120 de 0,5mm e 60 com 1,2mm discos (14 mm de diâmetro). 90 discos foram infiltrados com sílica pelo método sol-gel em temperatura ambiente (n = 30). A espessura do disco foi de 1,2 mm para os espécimes controle (espécime sem porcelana, n = 30). O recobrimento por porcelana feldspática foi de duas espessuras (0,5mm e 1 mm) sobre a zircônia que tinha 0,5 mm. Os espécimes com porcelana foram polidos com lixas de carbeto de silício (SiC) de granulação # 400, 600, 800 e 1200. Obtivemos 6 grupos: dois monolíticos (ZR- Zircônia Monolítica sem infiltração e ZRI- Zircônia Monolítica Infiltrada) (controle) e quatro estratificados: ZRF 1,0 (0,5mm Zircônia coberta com 0,5 mm porcelana), ZRIF 1,0 (0,5 mm Zircônia infiltrada coberta com 0,5 mm de porcelana), ZRF 1,5 (0,5 mm Zircônia infiltrada coberta com 1,0 mm de porcelana) ZRIF 1,5- Zircônia infiltrada (0,5 mm Zircônia infiltrada coberta com 1,0 mm de porcelana). Após o ensaio de flexão biaxial em meio aquoso, foram determinados o módulo de Weibull (m) e resistência característica (σθ). Os fragmentos foram analisados em EDS, MEV, DRX e FTIR. A Dureza (H) e tenacidade a fratura foram analisadas pela nanoindentação, já o módulo elástico (E) por duas técnicas, nanoindentação e por impulso, e para avaliar a adesão entre a zircônia e a porcelana foi aplicado o Teste de Scratch. Foram modeladas 7 condições experimentais e analisados pelo método por elementos finitos. A zircônia monolítica infiltrada mostrou uma estrutura com grãos arredondados envoltos em uma matriz de sílica, e a presença de zircônia cúbica e tetragonal. O DRX revelou a formação de ZrSiO4 nos grupos infiltrados. Os grupos monolíticos apresentaram módulos de Weibull superiores aos dos grupos com porcelana. Com a análise (AEF) não houve diferença entre os grupos com a mesma espessura, já para o grupo recoberto com 0,5 mm de porcelana, os valores de tração e compressão foram maiores. A cerâmica infiltrada apresentou microestrutura diferente, e a adesão da porcelana à zircônia não-infiltrada foi superior à da zircônia infiltrada.
  • The objective was to infiltrate silica in a Y- TZP ceramics, evaluate its effect on resistance biaxial strenght, and the union with feldspathic porcelain. For the analysis of flexural strength were prepared zirconia discs 180, 120 and 60 of 0.5 mm to 1.2 mm disks (14 mm diameter). 90 discs were infiltrated with silica by the sol-gel method at room temperature (n = 30). The thickness of the disk was 1.2 mm for the samples control (no porcelain specimen, n = 30). The coating was feldspathic porcelain by two thicknesses (0.5 mm and 1 mm) of zirconia, which had 0.5 mm. Specimens with porcelain were polished with sandpaper silicon carbide (SiC) granulation # 400, 600, 800 and 1200. We obtained six groups: two monolithic (Zr-Zirconia Monolithic without infiltration and ZRI- Zirconia monolithic Infiltrated) (control) and four laminated ZRF 1.0 (0.5 mm zirconia covered with 0.5 mm porcelain), ZRIF 1.0 (0.5 mm infiltrated zirconia covered with 0.5 mm of porcelain), ZRF 1.5 (0.5 mm infiltrated zirconia covered with 1.0 mm of porcelain) ZRIF 1,5-infiltrated Zirconia (0.5 mm infiltrated zirconia covered with 1.0 mm of porcelain). After the biaxial bending test in an aqueous medium were determined Weibull modulus (m) and the characteristic strength (σθ). The fragments were analyzed by EDS, SEM, XRD and FTIR. The hardness (H) and fracture toughness were analyzed by nanoindentation, since the elastic modulus (E) by two techniques, nanoindentation and on impulse, and to evaluate the adhesion between the zirconia and porcelain was applied Scratch Test. 7 experimental conditions were modeled and analyzed by the finite element method. The infiltrated zirconia showed a monolithic structure with rounded grain wrapped in a silica matrix, and the presence of cubic and tetragonal zirconia. The XRD showed the formation of ZrSiO4 infiltrates in groups. The monolithic modules Weibull groups showed superior to porcelain groups. With the analysis (FEA) there was no difference between the groups with the same thickness, for now the group covered with 0.5 mm of porcelain, the tensile and compressive values were higher. The infiltrated ceramic showed different microstructure, and the accession of porcelain to non- infiltrated zirconia was higher than the infiltrated zirconia.
Issue Date: 
15-Dec-2015
Publisher: 
Universidade Estadual Paulista (UNESP)
Keywords: 
  • Cerâmicas
  • Sílica gel
  • Porcelana dentária
  • Zircônio
  • Força compressiva
  • Resistência à tração
  • Falha de restauração dentária
  • Coroas
  • Propriedades químicas
  • Prótese dentária
  • Ceramics
  • Silica gel
  • Dental porcelain
  • Zirconium
  • Compressive strength
  • Tensile strength
  • Dental restoration failure
  • Dental crowns
  • Chemical properties
  • Dental prosthesis
URI: 
Access Rights: 
Acesso aberto
Type: 
outro
Source:
http://repositorio.unesp.br/handle/11449/132961
Appears in Collections:Artigos, TCCs, Teses e Dissertações da Unesp

There are no files associated with this item.
 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.