Retorque de parafusos de pilares protéticos com recobrimento de carbono tipo diamante: uma análise da manutenção do torque após fadiga mecânica

Abstract

The study analyzed the torque maintain of the screw abutments, with coating of diamond-like carbon (DLC) and doping of diamond (CD-DLC), submitted the retorque in external hexagonal (EH) and internal (IH) connections; after mechanical fatigue. HE and HI implants and different treatments of the abutments screws were divided into experimental groups (n = 5): untreated and not subjected to fatigue (EH-CON) (IHICON); fatigued untreatment (EH-CONF) (IH-CONF); fatigued with DLC (EH- DLCF) (IH-DLCF) and fatigued with CD-DLC (EH-CD-DLCF) (IH-CD-DLCF). The DLC and CD-DLC coating was deposited by plasma, PECVD method. Samples (Implant + abutment screew + metal crown), which had been exposed to 1 million fatigue cycles were retorquiadas, digital torque wrench, to the torque recommended by the manufacturer 30 N (HE) and 20 N (HI), and submitted again to 1 million cycles mechanics. At the end of fatigue, the screws were destorquiados to check the maintenance of torque. Screws from each experimental group were selected for observation by SEM. Statistical analysis was performed by ANOVA 2 Factors test (α = 0.05). There was no interaction among the factors studied (p = 0.765); the treatment of screws (p = 0.638) and the connection type (p = 0.615) showed no statistical difference. The microscopy images showed damage the threads and covering the presence of HI connections. Changes such as damage on the screws threads and film removal were observed among the experimental groups. The coating groups showed little or no damage on the screws threads. The DLC and CD-DLC coating did not interfere in the screw adaptation on the implant. Abutments screew coating with DLC and CD-DLC, after retorque, no raised torque maintenance

Esta pesquisa se propôs verificar a manutenção do torque, após fadiga mecânica, de parafusos de pilares protéticos com recobrimento de carbono tipo diamante (DLC) e com dopagem de diamantes (CD-DLC) submetidos ao retorque, em conexões hexagonais externa (HE) e interna (HI). Implantes HE e HI e diferentes tratamentos do parafuso protético foram alocados em grupos experimentais (n = 5): sem tratamento e não submetidos a fadiga (HE-CON) (HI-CON); sem tratamento fadigados (HECONF) (HI-CONF); com DLC fadigado (HE-DLCF) (HI-DLCF) e com CDDLC fadigados (HE-CD-DLCF) (HI-CD-DLCF). Os recobrimentos de DLC e CD-DLC foram depositados a plasma pelo método PECVD. As amostras (implante + parafusos + coroa metálica), que já haviam sido expostas a 1 milhão de ciclos de fadiga, foram retorqueadas com torquímetro digital, com o torque recomendado pelo fabricante 30 N (HE) e 20 N (HI), e submetidos novamente a 1 milhão de ciclos mecânicos. Ao término da fadiga, os parafusos foram destorqueados para verificar a manutenção do torque. Parafusos de cada grupo experimental foram selecionados para observação em MEV. A análise estatística foi realizada pelo teste Anova 2- Fatores (α = 0,05). Não houve interação entre os fatores em estudo (p = 0,765); o tratamento dos parafusos (p = 0,638) e o tipo de conexão (p = 0,615) não apresentaram diferença estatística. Alterações como danos nas roscas do parafuso e remoção do filme foram observados entre os grupos experimentais. Os grupos com revestimento apresentaram pouco ou nenhum dano nas roscas dos parafusos. O revestimento de DLC e CDDLC parece não ter interferido na adaptação do parafuso ao implante. Parafusos protéticos recobertos com DLC e CD-DLC, após o retorque, não elevaram a manutenção do torque