Effect of an experimental 4% titanium tetrafluoride varnish on dental erosion by a soft drink

Abstract

Objectives: This in vitro study assessed the effect of an experimental 4%TiF4 varnish on enamel erosion.Methods: Sixty bovine enamel blocks were randomly allocated to each type of varnish:Duraphat((R)) -D (NaF, 2.26%F), Duofluorid((R))-F(NaF, 2.71% F), TiF4-T(2.45%F) and no-fluoride-P. After application of the varnishes, the blocks were subjected to six sequential pH cycles (cola drink for 10 min and artificial saliva for 50 min, each) per day, during 4 days. After the pH cycles, the blocks were maintained in artificial saliva for 18 h. Enamel alterations were determined in the 2nd and 4th days, using profilometry (wear) and microhardness (%SMHC) tests. Data were tested using ANOVA and Tukey's tests (p < 0.05).Results: the mean %SMHC (+/- S.D.) at the 2nd and 4th day was, respectively, D (-77.26 +/- 5.04(a) and -88.59 +/- 5.11(A)), F (-76.79 +/- 7.82(a) and -88.78 +/- 6.10(A)), T(-88.28 +/- 3.19(b) and -92.04 +/- 2.54(A,B)) and P (-87.96 +/- 2.23(b) and -94.15 +/- 1.14(B)). The mean wear (mu m +/- S.D.) at the 2nd and 4th day was, respectively, D (3.16 +/- 0.32(a) and 7.56 +/- 0.90(A)), F(3.35 +/- 0.78(a,b) and 7.92 +/- 0.98(A)), T (3.81 +/- 0.43(b) and 7.69 +/- 0.76(A)) and P (3.43 +/- 1.13(a,b) and 7.31 +/- 0.53(A)).Conclusions: the NaF varnishes reduced the softening, but had no effect on the reduction of the wear. The TiF4 varnish was not able to reduce the softening and wear. (C) 2007 Elsevier Ltd. All rights reserved.