Title: 
Effects of electroplated zinc-nickel alloy coatings on the fatigue strength of AISI 4340 high strength steel
Author(s): 
Institution: 
Universidade Estadual Paulista (UNESP)
Abstract: 
It is well known that fatigue behaviour is an important parameter to be considered in mechanical components subjected to constant and variable amplitude loadings. In combination with corrosion phenomenon, fatigue effects were responsible for proximally 64% of fails that occur in metallic parts of aeronautical accidents in the last 30 years. Recovered substrates have been extensively used in the aerospace field. Cadmium electroplating has been widely applied to promote protective coatings in aeronautical components, resulting in excellent corrosion protection combined with a good performance in cyclic loading. Ecological considerations allied to the increasing demands for corrosion resistance, resulted in the search for possible alternatives. Zinc-nickel alloys received considerable interest recently, since these coatings showed some advantages such as a good resistance to white and red rust, high plating rates and acceptation in the market. In this study the effects of zinc-nickel coatings electroplated on AISI 4340 high strength steel were analysed on rotating bending and axial fatigue strength, corrosion and adhesion resistance. Compressive residual stress field was measured by a X-ray tensometry prior to fatigue tests. Optical microscopy images showed coating thicknesses, adhesion and the existence of an uniform coverage of nearly all substrates. The fractured fatigue specimens were investigated using a scanning electron microscope. Three different zinc-nickel coating thicknesses were tested and comparison with rotating bending fatigue data from specimens cadmium electroplated and heat treated at 190°C for 3, 8 and 24 hours to avoid the diffusion of hydrogen in the substrate, was performed. Experimental results showed effect of coatings on the AISI 4340 steel behaviour when submitted to fatigue testing and the existence of coating thickness influence on the fatigue strength.
Issue Date: 
1-Dec-2005
Citation: 
11th International Conference on Fracture 2005, ICF11, v. 4, p. 2599-2604.
Time Duration: 
2599-2604
Keywords: 
  • Adhesion resistance
  • Aeronautical components
  • Aerospace field
  • AISI 4340 steel
  • Axial fatigue
  • Cadmium electroplating
  • Coating thickness
  • Compressive residual stress
  • Corrosion phenomena
  • Cyclic loadings
  • Fatigue behaviour
  • Fatigue effects
  • Fatigue specimen
  • Fatigue strength
  • Mechanical components
  • Metallic part
  • Plating rates
  • Rotating bending
  • Rotating bending fatigue
  • Scanning Electron Microscope
  • Tensometry
  • Uniform coverage
  • Variable amplitude loading
  • Zinc-nickel
  • Zinc-nickel alloys
  • Adhesion
  • Aerodynamics
  • Cadmium
  • Cadmium plating
  • Corrosion resistance
  • Electroplating
  • Fatigue testing
  • Fracture
  • High strength steel
  • Hydrogen
  • Nickel alloys
  • Nickel coatings
  • Optical microscopy
  • Protective coatings
  • Scanning electron microscopy
  • Steel testing
  • Substrates
  • Thickness measurement
  • Zinc
  • Zinc coatings
  • Bending strength
URI: 
Access Rights: 
Acesso restrito
Type: 
outro
Source:
http://repositorio.unesp.br/handle/11449/68677
Appears in Collections:Artigos, TCCs, Teses e Dissertações da Unesp

There are no files associated with this item.
 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.