In vitro evaluation of apical microleakage using different root-end filling materials

Abstract

The objective of this study was to evaluate the apical leakage of retrograde cavities filled with Portland Cement (Concrebrás S/A-MG-Brazil), ProRoot MTA™ (Dentsply International, Johnson City, TN, USA) and Sealapex (Kerr Corporation, Orange, California, USA) with addition of zinc oxide (Odahcam Herpo Produtos Dentários Ltda, Rio de Janeiro, RJ, Brazil). Forty-two extracted single-rooted human teeth were decoronated and used for this study. The root canals were instrumented at 1.0mm short of the apical foramen using the step-back technique to an apical ISO size 60. The roots were obturated with gutta-percha points and sealer Sealapex (Kerr Corporation-USA) and then 3mm of each root apex was sectioned at a 90° angle. Ultrasonic retrograde preparation was performed with a diamond tip to 3mm depth and the roots were randomly divided into 3 groups according to the filling material: G1-Portland, G2-ProRoot MTA, G3- Sealapex zinc oxide-added cement. The root surfaces were covered with nail varnish up to 2mm from the apical foramen, immersed in simulated tissue fluid for 30 days, and then immersed in 0.2% Rhodamine B solution for 24 hours for evaluation of marginal leakage. The results showed mean leakage of 0.75, 0.35 and 0.35 for groups 1, 2 and 3, respectively; however, Kruskal-Wallis test revealed that there was no statistically significant difference among the results (p>0.05).