Please use this identifier to cite or link to this item: http://acervodigital.unesp.br/handle/11449/30017
Full metadata record
DC FieldValueLanguage
dc.contributor.authorSantos, C.-
dc.contributor.authorSouza, J. V. C. de-
dc.contributor.authorKelly, C. A.-
dc.contributor.authorRibeiro, S.-
dc.contributor.authorSilva, O. M. M.-
dc.contributor.authorSilva, C. R. M.-
dc.contributor.authorStrecker, K.-
dc.date.accessioned2014-05-20T15:16:23Z-
dc.date.accessioned2016-10-25T17:50:11Z-
dc.date.available2014-05-20T15:16:23Z-
dc.date.available2016-10-25T17:50:11Z-
dc.date.issued2005-12-01-
dc.identifierhttp://dx.doi.org/10.1590/S0366-69132005000400017-
dc.identifier.citationCerâmica. Associação Brasileira de Cerâmica, v. 51, n. 320, p. 413-419, 2005.-
dc.identifier.issn0366-6913-
dc.identifier.urihttp://hdl.handle.net/11449/30017-
dc.identifier.urihttp://acervodigital.unesp.br/handle/11449/30017-
dc.description.abstractO objetivo desse trabalho foi a preparação in situ do compósito alfa-SiAlON-SiC com desenvolvimento de solução sólida de nitreto de silício (SiAlON) durante a sinterização, utilizando o óxido misto de ítrio e terras raras (CRE2O3), fabricado na FAENQUIL, como estabilizador da fase alfa-Si3N4. Uma fração de 20% em volume da mistura AlN-CRE2O3, na proporção 9:1 (mol%), foi misturada a 80% em volume de Si3N4. A essa mistura (Si3N4-AlN-CRE2O3), foram adicionadas quantidades variadas de beta-SiC (entre 0 e 20 peso%). As misturas de pós foram moídas e, em seguida, compactadas por prensagem uniaxial e, subseqüente prensagem isostática a frio. Os compactos foram submetidos a sinterização a 1950 0C por 1 h e sob pressão de 1 MPa de N2. As amostras sinterizadas foram caracterizadas quanto às fases presentes, transformação Si3N4-SiAlON e aspectos microestruturais. Os resultados revelaram alfa-SiAlON e beta-SiC como únicas fases cristalinas. Além disso, não houve cristalização parcial da fase intergranular remanescente, e observou-se que variadas adições de SiC não interferiram na solubilidade e conseqüente formação de alfa-SiAlON, porém o crescimento de grãos alongados de alfa' é inibido em função da adição de quantidades maiores de SiC.pt
dc.description.abstractThe objective of this work is to obtain in situ alpha-SiAlON-SiC composites, by silicon nitride solid solution development, during sintering, using rare earth and yttrium oxide mixture (CRE3O3) as stabilizer of the alpha-Si3N4 phase. A fraction of 20 vol.% of AlN-CRE2O3 mixture was mixed to 80 vol.% of Si3N4. Different contents of beta-SiC powders were mixed to the Si3N4-AlN-CRE2O3 powder mixture. The powder mixtures were milled and compacted by uniaxial and cold isostatic pressing. The green bodies were sintered at 1950 °C during 1 h under 1 MPa of N2 pressure. The sintered samples were characterized by X-ray diffraction and scanning electron microscopy, in order to assess the crystalline phases and microstructural aspects, respectively. The results revealed the presence of alpha-SiAlON and beta-SiC as the only crystalline phases present in the material. No partial crystallization of remaining intergranular phase was detected. No alpha-SiAlON solubility variation was observed by the use of different SiC contents, but different grain of a' grains are related to SiC addition in the mixtures.en
dc.description.sponsorshipFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)-
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)-
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)-
dc.format.extent413-419-
dc.language.isopor-
dc.publisherAssociação Brasileira de Cerâmica-
dc.sourceSciELO-
dc.subjectsinterizaçãopt
dc.subjectCRE2O3pt
dc.subjectcompósito alfa-SiAlON-SiCpt
dc.subjectmicroestruturapt
dc.subjectsinteringen
dc.subjectCRE2O3en
dc.subjectalpha-SiAlON-SiC compositesen
dc.subjectmicrostructureen
dc.titleObtenção in situ do compósito alfa-SiAlON-SiCpt
dc.title.alternativeIn situ preparation of alpha-SiAlON-SiC compositeen
dc.typeoutro-
dc.contributor.institutionUniversidade de São Paulo (USP)-
dc.contributor.institutionUniversidade Estadual Paulista (UNESP)-
dc.contributor.institutionCentro Técnico Aeroespacial Div. Materiais AMR-
dc.description.affiliationFAENQUIL DEMAR-
dc.description.affiliationUNESP FEG-
dc.description.affiliationCentro Técnico Aeroespacial Div. Materiais AMR-
dc.description.affiliationUnespUNESP FEG-
dc.identifier.doi10.1590/S0366-69132005000400017-
dc.identifier.scieloS0366-69132005000400017-
dc.rights.accessRightsAcesso aberto-
dc.identifier.fileS0366-69132005000400017.pdf-
dc.relation.ispartofCerâmica-
Appears in Collections:Artigos, TCCs, Teses e Dissertações da Unesp

There are no files associated with this item.
 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.